Composition and method for inducing bone growth and healing

ABSTRACT

A composition and method for inducing bone growth and healing is provided. The composition is useful for promoting new bone synthesis, and to enhance the mechanical stability and longevity of orthopaedic implants. The composition includes a bone endogenous material which is used as raw material for the body&#39;s natural osteogenic mechanism to synthesize new bone. The composition has a flow phase and a congealed phase. The composition is applied, in the flow phase, within the reamed medullary canal of a long bone prior to insertion of an endoprosthesis. Following insertion of the endoprosthesis, the composition undergoes a phase change to the congealed phase, for example via cross-linking of the bone endogenous material in the composition, to provide a compliant barrier layer in the intra-medullary gap between the implanted endoprosthesis and the medullary canal wall. The resulting barrier layer has a dual mode porosity system, having a first order porosity to accommodate and promote convective diffusion of nutrient species into and through the barrier layer, and a second order porosity to accommodate osteoblastic migration therein without the need for osteoclastic resorption. Osteoblasts synthesize new bone using the barrier layer itself as raw material, essentially osteoconverting the barrier layer into synthesized new bone. In a preferred embodiment, the second order porosity is provided via a rapidly degrading polymer added to the composition, which has a half-life for degradation of 1-60 days.

This application claims the benefit of U.S. Provisional Patent Application Ser. No. 60/358,160 filed Feb. 20, 2002, which is hereby incorporated by reference in its entirety.

The invention relates to a composition that induces bone growth and healing. More particularly, it relates to a composition that facilitates rapid bone healing and adhesion to a non-cemented endoprosthetic implant. Such a composition preferably facilitates osteoconduction toward a non-cemented endoprosthetic implant by enhanced molecular transport and cellular mechanical loading via load-induced fluid flow to promote implant stability and longevity.

BACKGROUND OF THE INVENTION

It is often necessary to implant an endoprosthetic device within the living bone of a patient, e.g. during a hip replacement surgery. In this procedure, the medullary canal within the bone is first reamed as known in the art, and then an endoprosthesis having a long shaft is thrust into the reamed canal to form an interference fit therein.

Unfortunately, this interference fit method of endoprosthetic implantation often results in a poor fit between the prosthesis and surrounding bone tissue, resulting in a gap at the interface between the bone and the prosthesis. What starts as micromotion, typically in the proximal area of the implant, can result in instability of the implant over time. As the implant becomes looser and more unstable within the medullary canal, it moves increasingly back and forth from cyclic loading within the medullary canal, grinding against the surrounding bone tissue. This can result in both mechanical wear and osteoclastic resorption of surrounding bone tissue, further compounding endoprosthetic instability. The short-term result is enhanced pain for the patient, and the ultimate result is a failure of the endoprosthetic implant which must be replaced surgically. However, surgical replacement becomes more difficult with each failure because the prior reaming of the medullary canal and loosening of the implant through osteoclastic resorption greatly reduce the amount and quality of available bone tissue to anchor the implant.

In addition, endoprosthetic implantation has traditionally been limited largely to the elderly population. Therefore, in the past, endoprostheses were not usually required or expected to have useful lives longer than about 10-15 years. However, it is becoming more common to implant endoprostheses in younger patients, for example in young adults 18-50 years of age. It is desirable, especially for younger patients, that endoprostheses have a useful lifespan longer than the traditional 10-15 years, preferably at least 20, 25, or 30 years, or longer. Accordingly, there is a need in the art for a material to fill the gap between an endoprosthetic implant and the surrounding bone tissue in the medullary canal that provides a longer useful life for the implant. Such a material preferably will speed healing of bone tissue in the medullary canal following implantation, and most preferably it will promote bone growth and adhesion toward (preferably to) the implant itself.

SUMMARY OF THE INVENTION

A composition is provided having a bone endogenous material and a degradable polymer material. The degradable polymer material has a half-life for degradation of 1-30 days.

A method of promoting osteogenesis is also provided including the steps of: a) providing a composition having a bone endogenous material in a flow phase; b) applying the composition to a site within a patient where it is desired to synthesize new bone; c) the composition undergoes a phase transformation from the flow phase to a congealed phase; and d) providing a dual mode porosity system in the composition in its congealed phase, wherein the congealed phase of the composition has a first order porosity and a second order porosity.

A compliant barrier layer in an intra-medullary gap between a medullary canal wall of a bone and an endoprosthesis implanted within the medullary canal is also provided. The compliant barrier layer includes a bone endogenous material, and has a dual mode porosity system with a first order porosity and a second order porosity. The said second order has a larger mean Stokes diameter than the first order porosity.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows, diagrammatically, a longitudinal cross-section of a long bone having an endoprosthetic implant therein, as well as a compliant barrier layer made from the bone healing composition according to the invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS OF THE INVENTION

As used herein, when a preferred range is given, such as 5-25 (or 5 to 25), this means preferably at least 5 and, separately and independently, preferably not more than 25.

The invention comprises a composition that is effective to induce bone healing and bone growth, as well as to enhance the mechanical stability and longevity of orthopaedic implants. This composition is referred to as “bone prime” herein because in a preferred embodiment it is used to prepare or ‘prime’ the reamed medullary canal within a long bone to receive and accommodate an endoprosthetic shaft therein. The composition provides a semi-rigid, compliant barrier layer in the annulus or annular gap between the endoprosthetic shaft and the medullary canal wall, which barrier layer promotes osteoconduction and bone growth from the bone toward (and to) the prosthesis as will be described. The bone primer can be provided within the medullary canal prior to introduction of the endoprosthetic, it can be applied or coated onto the endoprosthetic surface, and/or the inner surface of the bone prior to implantation as will become apparent from the disclosure.

Referring to FIG. 1, the bone primer composition provides or results in a compliant barrier layer 10 in the intra-medullary gap 12 between the medullary canal wall 14 and an endoprosthetic surface 16. The medullary gap 12 is shown exaggerated for ease of visualization.

In a preferred embodiment, the inventive composition comprises at least 40, preferably at least 50 or 60, weight percent (dry basis) of a bone endogenous material. The composition also includes an effective amount of a degradable polymer material sufficient to produce a second order porosity in the compliant barrier layer 10 upon degradation (explained below), and a quantify of trophic factors, such as growth factors, in an effective amount to induce osteoblast migration and promote osteointegration of the endoprosthetic implant (also explained below).

The bone endogenous material can be or include any material that is normally found in healthy human bone tissue as biologically occurring molecules. The bone endogenous material can be naturally occurring (for example harvested from a patient) or synthetically prepared via conventional techniques. In particular, the bone endogenous material used in the bone primer composition of the present invention can be or include fibronectin, collagen, laminin, tenascin, proteoglycans, glycosaminoglycans, fibrinogen, hyaluronic acid, elastin, tricalcium phosphate, hydroxyapatite, as well as other extracellular bone matrix materials. The bone endogenous material can also be or include other naturally derived materials such as alginates, vitrogens, vitronectins, and chitosans. The endogenous material can also be a mixture of any of the above materials.

The degradable polymer material can be or include any natural or synthetic degradable polymer that is non- or substantially non-immunogenic. Preferably, the degradable polymer material has a half-life for degradation of 1-60 days, preferably 1-30 days, preferably 1-20 days, preferably 1-14 days, preferably 1-7 days. Suitable degradable polymers include polylactic acid (PLA), polyglycolic acid (PGA), polyanhydrides, polyvinyl alcohol (PVA), poly [L-lactic acid] (PLLA), poly [D,L-lactic acid] (PDLLA) and poly (lactide-co-glycolide) copolymer (PLGA). Alternatively, the degradable polymer material can be or include naturally biologically occurring polymeric species such as chitosan, agarose and alginate.

Growth factors for use in the present invention include BMP-7, BMP-4, PDGF-BB, TGF-β1, tetracycline, bFGF, VEGF, PTH, and PTH-rp. Mixtures of the above can also be used. The growth factors can be in globular protein form or active peptide fragments that promote bone regeneration. There are several distinct advantages of the peptide form. In the peptide form, the factors lack immunogenicity. In addition, small peptide molecules are readily diffusible, and exhibit less promiscuity (i.e. greater specificity) because they can be designed for specificity via conventional techniques. The globular protein form also has several distinct advantages, including tertiary structure, enhanced conformation, and slower rate of uptake and potentially of metabolism.

Preferably, the bone primer composition can also be provided with medicaments, such as antibiotics and/or analgesics. Also preferably, the bone primer composition can be provided with other osteogenic and/or angiogenic nutrients, e.g. glucose, amino acids, glucosamines, etc.

The invented bone primer composition preferably has two material phases; a flow phase and a congealed or semi-solid phase. By flow phase, it is meant that the composition is generally a liquid, preferably a viscous liquid having a viscosity of at least 1, preferably at least 10, preferably at least 100, preferably at least 300, preferably at least 500, preferably at least 700, preferably at least 800, preferably at least 900, preferably at least 1000, cP at 25° C. Such a composition is easily applied within the medullary canal by a surgeon during or prior to implantation of an endoprosthetic device 30. Also, high viscosity minimizes or substantially eliminates air bubble entrainment within the composition as it is poured or delivered into the medullary canal. By congealed phase, it is meant that the composition exists in a solid or pseudosolid or semi-solid material, e.g. a gelatinous material, that no longer flows but is substantially fixed in its dried or congealed form.

Preferably, the bone primer composition is applied within the medullary canal 18 during or prior to endoprosthesis implantation. The procedure is generally as follows. First, the bone 20 that is to receive the endoprosthetic implant 30 is prepped in a conventional manner. Typically, preparation includes resection of the bone end, for example in knee replacement, or femoral/humeral head resection for hip/elbow replacement, followed by the widening and/or reaming of the medullary canal 18 within the bone 20.

Second, a quantity of the invented bone primer composition, in the flow phase, is applied or introduced within the reamed medullary canal 18 by conventional cementing techniques until the composition fills or substantially fills the canal 20. Preferably, the composition is provided in the medullary canal 18 prior to insertion of the endoprosthesis therein. Third, the endoprosthesis is inserted in a conventional manner. It will be understood that insertion of the prosthesis into the medullary canal 20 will result in extrusion of excess bone primer composition up to the excluded volume of the endoprosthesis 30 in the medullary canal. In this manner, the bone primer composition completely fills the intra-medullary gap 12 between the implanted prosthesis 30 and the surrounding medullary canal wall 14, minimizing entrained air bubbles. As stated above, the composition is preferably in the flow phase when it is provided (e.g. by pouring, via a syringe, or extrusion through a tube opening) in the medullary canal.

Once the medullary canal is completely (or substantially completely) filled with the invented bone primer composition, the endoprosthesis 30 is inserted in a conventional manner as explained above, and excess or extruded bone primer composition is wiped away.

Following endoprosthesis insertion, the bone primer composition in the intra-medullary gap 12 between the prosthesis and the medullary canal wall 14 preferably undergoes a phase transformation (e.g. sets or polymerizes), into the congealed phase. In the congealed phase, the bone primer composition provides the compliant barrier layer 10 in the medullary gap 12 as shown in FIG. 1, substantially filling the intra-medullary gap 12. The barrier layer 10 preferably completely or substantially completely encapsulates the implanted endoprosthesis 30.

The compliant barrier layer 10 is also preferably porous, preferably having a dual mode porosity that imbibes or is effective to imbibe interstitial fluid from surrounding tissue. Dual mode porosity means that the compliant barrier layer made from the invented bone primer composition in the congealed phase has a first order porosity to accommodate or promote molecular diffusion between the medullary canal wall 14 and the endoprosthetic surface 16, as well as to promote bulk fluid flow or fluid imbibement therebetween, and a second order porosity that provides a pathway through which osteoblasts can enter the medullary gap 12 without the requirement of prior osteoclastic resorption. Preferably, the first order porosity has a first order radial porosity gradient with first order porosity increasing in a radially inward direction from the medullary canal wall 14 to the endoprosthetic surface 16, e.g. with the first order mean Stokes pore diameter increasing from approximately 0.1-20×10⁻¹⁰, preferably 0.5-15×10⁻¹⁰, preferably 1-10×10¹⁰, preferably 2-8×10¹⁰, preferably 3-7×10⁻¹⁰, preferably 4-6×10⁻¹⁰, preferably about 4-5×10⁻¹⁰, meters adjacent the medullary canal wall 14, to 50-300×10⁻¹⁰, preferably 60-250×10⁻¹⁰, preferably 70-200×10⁻¹⁰, preferably 80-150×10⁻¹⁰, preferably 90-120×10⁻¹⁰, preferably about 100×10⁻¹⁰, meters adjacent the endoprosthetic surface 16. Preferably, for the first order porosity, the pore size adjacent the canal wall 14 is sufficient to accommodate 300-400 Da molecular weight species, and the pore size adjacent the prosthesis wall 16 is sufficient to accommodate species having greater than 40 kDa molecular weight. Alternatively, the first order radial porosity gradient can be provided as a pore density gradient with increasing pore density toward the implant surface 16. This serves to promote imbibement from the natural bone tissue at the canal wall 14 toward the implant surface 16.

It has been found that the above-described radial first order porosity gradient can be induced by providing a radial temperature gradient during phase transformation from the flow phase to the congealed phase. By heating the prosthesis, e.g. to 40° C., prior to insertion in the medullary canal filled with the bone primer composition, a radial temperature gradient is induced in the surrounding composition. The magnitude and direction of the porosity gradient can be controlled as a function of the magnitude and direction of the temperature gradient. The direction of the temperature gradient can be controlled by either heating or cooling the prosthesis relative to the canal wall 14 prior to insertion. Alternatively, either the canal wall 14 or the prosthesis surface 16 can be coated with a cross-linking agent to promote increased cross-linking of the bone primer composition adjacent that surface, thereby decreasing the porosity of the barrier layer 10 adjacent that surface. The slope of the first order porosity gradient can be controlled by selecting cross-linking agents with suitable kinetics and rate of diffusion in the bone primer composition. In a further alternative embodiment, the porosity gradient can be provided by taking advantage of thixotropic properties of the bone primer composition (differential in shear stress during application produces differences in pore size distribution), or of the different electrochemical properties of the bone and the prosthesis.

The second order porosity preferably comprises a tortuous network of relatively large-pore passages compared to the first order porosity, i.e. preferably having a mean Stokes diameter on the order of 10⁻⁶ meters. The second order porosity in the invented compliant barrier layer 10 provides a tunnel network for the mobilization of osteoblasts from the medullary canal wall 14 through the barrier layer 10 toward the endoprosthetic surface 16. By providing the second order porosity, the osteoclastic resorption step that typically must precede osteoblastic bone synthesis in the ordinary biological process of bone remodeling is preferably reduced or diminished, more preferably substantially eliminated. The result is the minimization of bone consumption or resorption mechanisms (i.e. osteoclastic resorption) and the maximization of bone synthesis mechanisms. In addition, the second order porosity provides a pathway for angiogenic species (such as angiogenesis-stimulating growth factors) and the synthesis of blood flow pathways to osteoblastic synthesis sites. Simultaneously, the first order porosity promotes molecular diffusion of nutrient species required by the osteoblasts in order to synthesize new bone, preferably from the bone endogenous material present in the barrier layer 10. As stated above, the bone primer composition (and therefore the resulting compliant barrier layer 10) preferably comprises, or is made substantially from, a bone endogenous material. As a result, osteoblasts can synthesize new bone directly from the barrier layer material, resulting in the fusion of the surrounding bone to the implanted endoprosthesis 30.

This feature of the present invention represents a significant advance over the prior art. In uncemented arthroplasty, a press fit is achieved between the bone and the prosthesis leaving a gap of up to approximately 2 mm between the implant surface and bone. Alternatively, in the conventional cemented arthroplasty procedure, a bone cement such as polymethyl methacrylate (PMMA) is used to cement an endoprosthesis within a reamed medullary canal, with the reamed canal typically being provided with a slightly smaller diameter than the prosthesis resulting in an interference fit. The interference fit is to ensure intimate contact with the methacrylate cement for both the prosthetic surface and the canal wall. In this conventional technique, bone from the canal wall is not induced to grow toward the implant, or to fill in imperfections or gaps between the prosthesis and the canal wall. In fact, the methacrylate cement layer between the canal wall and the prosthesis is a barrier to the transduction of biological species responsible for generating new bone, such as osteoblasts and osteoblastic nutrients.

Conversely, the present invention provides a compliant barrier layer 10 between the endoprosthetic surface and the canal wall that is substantially made from bone endogenous material, and has the dual mode porosity system described above. The dual mode porosity system permits and actually affirmatively promotes or induces osteoconduction from the canal wall 14 toward (and to) the endoprosthetic surface 16, using the barrier layer 10 itself as the raw material for bone synthesis. Thus, it can be seen that in addition to providing a means of fixing the prosthesis in place, the barrier layer 10 of the present invention effectively promotes osteoconduction via the body's own natural osteogenic mechanism, provides pathways for osteoblastic migration via the second order porosity, and provides pathways for nutrient and growth factor migration via diffusion and convection through the first order porosity. Ultimately, the entire barrier layer 10 is essentially converted to new bone via the body's own osteogenic mechanism, resulting in an effective osteointegration of the endoprosthetic implant within the surrounding bone. In other words, once all of the bone endogenous material in the barrier layer 10 has been used by osteoblasts to synthesize new bone, the end result is a continuous living bone that has grown inward toward and the implant which has now been effectively integrated within the bone, without no or substantially no presence of any interfacial barrier layer remaining between the bone and the implant. This result has never before been possible because the interfacial cement layers of the prior art made true osteointegration of endoprostheses (bone growth all the way up to the implant) impossible.

An additional advantage over conventional bone cements is that the invented barrier layer is a compliant layer, and is less prone to stress fracturing or failure from shearing forces under heavy or impact loading. It is important that the barrier layer 10 is compliant because osteoblastic bone synthesis (osteogenesis) will not occur immediately. It is thus highly desirable to provide a shock-absorbing or “damping” medium between the endoprosthesis 30 and the surrounding bone 20 prior to complete osteoconversion of the barrier layer 10 via osteogenesis. This ensures that the endoprosthesis will not loosen or become unstable in the interim due to stress concentration effects (e.g. through abrupt changes in mechanical properties at the implant-bone interface) or micromotion at the implant-bone interface. The compliant barrier layer 10 also ensures that interstitial fluid containing nutrients and growth/angiogenic factors is pumped between the implant surface and bone (e.g. like compressing and releasing a fluid-filled sponge), and that there is adequate bone-endogenous material in situ for the synthesis of new bone to completely fill the intra-medullary gap 12. Preferably, the compliant barrier layer 10 exhibits strains of 0.01-2.0, preferably 0.01-1.8, preferably 0.01-1.6, preferably 0.01-1.4, preferably 0.01-1.2, preferably 0.01-1.0, preferably 0.01-0.8, preferably 0.01-0.6, preferably 0.015-0.4, preferably about 0.02-0.2% during normal physiologic loading, e.g. from walking.

The mechanism by which the dual mode porosity is believed to promote osteoconduction and conversion of the barrier layer 10 will now be described. The first order porosity gradient as described above promotes mechanical loading-induced mass transport of nutrient species (e.g. glucose, amino acids, oxygen, etc.) required for osteoblastic and angiogenesis metabolism from the medullary canal wall 14 toward the endoprosthetic surface 16. Specifically, the mechanical loading of a bone (e.g. a bone having an endoprosthesis implanted therein) induces bulk fluid flow as well as molecular diffusion or convective perfusion of diffusive species through the bone's pore structure. This property of bone is generally known in the art, and is described, e.g. in the following publications, all of which are incorporated herein by reference:

-   Knothe Tate, M. L., Niederer, P., and Knothe, U., “In Vivo Tracer     Transport Through the Lacunocanalicular System of Rat Bone in an     Environment Devoid of Mechanical Loading”, Bone, Vol. 22, No. 2, pp.     107-117, February 1998; -   Knothe Tate, M. L., Knothe, U., and Niederer, P., “Experimental     Elucidation of Mechanical Load-Influenced Fluid Flow and Its     Potential Role in Bone Metabolism and Functional Adaptation”, Am. J.     Med. Sci., Vol. 316, No. 3, pp. 189-195, September 1998; -   Knothe Tate, M. L., and Knothe, U., “An ex vivo model to study     transport processes and fluid flow in loaded bone”, J. Biomech.,     Vol. 33, pp. 247-254, 2000; -   Knothe Tate, M. L., Steck, R., Forwood, M. R., and Niederer, P., “In     Vivo Demonstration of Load-Induced Fluid Flow in the Rat Tibia and     Its Positional Implications for Processes Associated with Functional     Adaptation”, J. Exp. Biol., Vol. 203, pp. 2737-2745, 2000; and -   Knothe Tate, M. L., “Interstitial Fluid Flow”, Chapter 22, (pp.     22-1-22-29) Bone Mechanics Handbook, Cowin, Stephen C., Ed., CRC     Press, New York, 2001.

In addition, without wishing to be bound by a particular theory, it is believed that fluid flow in bone proceeds by one or several of the mechanisms outlined in the paper entitled “Whither Flows the Fluid in Bone?” An Osteocyte's Perspective, by Melissa Knothe Tate, Ph.D., contained in U.S. Provisional Patent Application Ser. No. 60/358,160 filed Feb. 20, 2002, incorporated by reference hereinabove.

The inventive composition is prepared initially as an aqueous mixture, e.g., a slurry, suspension, hydrogel, or any other suitable form of aqueous composition. The bone endogenous material is supplied as a powder and suspended via conventional techniques to provide the aqueous mixture. Preferably, this mixture has a viscosity of at least 100 cP or 1000 cP. In a preferred embodiment, the degradable polymer material mentioned above (to provide the second order porosity) is added to the mixture and is admixed to substantially uniformly distribute the degradable polymer throughout the mixture. Upon congealing or setting from the flow phase to the congealed phase, the rapidly degrading polymer rapidly degrades leaving a tortuous network of tunnels or pores throughout the compliant barrier layer 10 to accommodate bulk fluid flow and migration of large cellular species, e.g. osteoblasts. The amount of degradable polymer that is added to the mixture is selected such that the resulting second order porosity (the tunnels left behind in the barrier layer 10 once the polymer has completely degraded) represents a void fraction of 2-40, preferably about 3-30% relative to the total volume of the barrier layer 10 based on said second order porosity. The degradable polymer material is preferably supplied in the form of microspheres or small particulates whose particle size is selected to correspond to the desired pore-size diameter for the second order porosity tunnel network.

This rapidly degrading polymer can be (and preferably is) formulated to include chemical species that are found naturally within osteoclastic resorption lacunae, e.g. TRAP (tartrate resistant acid phosphatase). Such chemical species are left behind within the tortuous pore network following polymeric degradation, where they promote and help direct osteoblastic synthesis of new bone. The second order porosity is important to provide a migratory network for osteoblasts, in order that osteoclasts are not necessary to consume bone or bone primer material in order for the osteoblasts to travel through the barrier layer 10 and to reach the endoprosthetic surface 16. As stated above, the degradable polymer preferably has a half-life of 1-60 days, more preferably about 1-7 days. In general, the shorter the polymer half-life the better, (e.g., it can be less than 1 day) so long as it does not substantially degrade before a surgical implant procedure can be completed. A half-life of 1 day is believed to be long enough to prevent any complications resulting from too rapid polymer degradation. Too long a half-life, e.g. greater than 60 days, and one risks the body's own bone remodeling mechanism will introduce osteoclasts to provide tunnels through the barrier layer 10 via osteoclastic resorption to provide pathways for the osteoblasts.

Alternatively to the degradable polymer, the second order porosity can be provided in the compliant barrier layer 10 via conventional leaching techniques. For example, a leachable particulate species, e.g. a salt compound, can be provided in the bone primer composition mixture in place of the degradable polymer. The salt compound (such as NaCl) is then leached out via conventional techniques such as osmosis leaving behind the tortuous second order porosity network. Leaching methods and leachable species are well known in the art, and any suitable conventional leaching method or species could be used.

The trophic (growth) factors are also provided in the mixture in conventional amounts which are known or ascertainable to a person of ordinary skill in the art based on the present disclosure, such that an effective amount of growth factors is provided to promote osteogenesis as soon as possible after the composition congeals to provide the barrier layer 10 as described above.

In a preferred embodiment, the growth factors are provided by covalently linking the factors to polyethylene glycol (PEG) chains. PEG is a flexible hydrophilic polymer. The growth factor-linked PEG species are then incorporated into the mixture and admixed therein. Upon forming the congealed phase, the PEG chains are covalently bonded to the pore surfaces within the first order porosity of the barrier layer scaffold. According to this embodiment, the growth factors are fixed in place in a uniform distribution throughout the scaffold. By fixing the growth factors in this manner via PEG chains, the growth factors cannot diffuse away or become metabolized. The fixed growth factors are available as exposed ligands that can bind surface receptors of approaching osteoblasts in order to promote osteogenesis at the growth factor fixation site. In other words, the uniform, fixed distribution of growth factors throughout the bone endogenous material scaffold of the barrier layer 10 provides a lure for traveling osteoblasts to synthesize bone at the growth factor fixation sites, ensuring substantially complete osteoconversion of the barrier layer into synthesized new bone.

In another preferred embodiment, the growth factors are loaded into the microspheres or particulates of the degradable polymer responsible for providing the second order porosity described above. As the polymer degrades, the growth factors are left behind, initially concentrated within the newly formed second order porosity network of the bone endogenous material scaffold. In this embodiment, the release of the growth factors within the barrier layer 10 is controlled by the rate of degradation (the half life) of the degradable polymer, which in turn limits the rate of growth factor metabolism. A key advantage to this embodiment is that because the growth factors are initially highly concentrated within the second order porosity, they are readily and immediately available to osteoblasts (which travel through the second order porosity network) which use them in osteogenesis. This embodiment may promote more rapid osteogenesis due to the immediate availability of growth factors for chemotaxis and migration of osteoblasts in the second order porosity network.

Preferably, the bone primer composition mixture can also be provided with a medicament, such as an antibiotic or analgesic, to be slowly released following endoprosthetic implantation. Also preferably, the bone primer composition can be provided with other osteogenic and/or angiogenic nutrients, e.g. glucose, amino acids, etc.

Once the aqueous mixture has been prepared, it is delivered to the medullary canal in the flow phase as described above, and the endoprosthesis is inserted. Following endoprosthetic insertion, the composition undergoes a phase transformation from the flow phase to the congealed phase to provide the invented barrier layer 10 and to securely retain the endoprosthesis therein. The phase change mechanism can be designed according to any suitable mechanism for gellation of a flowable phase in vivo, so long as the gellation mechanism is biocompatible. A preferred gellation mechanism is to use a cross-linking agent to cross-link the bone endogenous material molecules to thereby provide the congealed phase. Suitable cross-linking agents include thrombin, NDGA, DOPA, lysyl oxidase, genipin, microwaves, ultraviolet (UV) light, prolyl hydroxylase, and horseradish peroxidase. The cross-linking agent is selected based on the principal bone endogenous material or materials to provide a functionally cross-linked scaffold from the bone endogenous material(s). In a preferred embodiment, the bone primer composition mixture (flow phase) is prepared separately from the cross-linking agent, and each is delivered in the medullary canal so that they first meet and are mixed within the canal. A double-barrel syringe as known in the art can be used for this purpose, such that the bone primer composition and the cross-linking agent are mixed upon elution from the syringe as they are being delivered into the medullary canal.

Following cross-linking in the medullary gap between the canal wall 14 and the endoprosthesis 16, the bone endogenous material forms the structural backbone or scaffold for the compliant barrier layer 10, and has a characteristic material porosity based on the bone endogenous material, the cross-linking agent used and the degree of cross-linking (e.g. 100% cross-linking results in lowest porosity whereas a lesser degree of cross-linking results in higher porosity). The inherent material porosity of the cross-linked bone endogenous material provides the first order porosity described above, through which nutrient and other species, are induced to diffuse through the barrier layer 10 as a result of cyclical loading of the bone. The degree of cross-linking, and therefore the first order porosity, can be tuned or controlled by varying the amount of cross-linking agent used, temperature, pH, as well as other reaction parameters.

Another highly beneficial effect of this cross-linking is that it promotes or increases the initiation of calcification at the endoprosthesis/barrier layer interface. This calcification ultimately results in cross-linked material between synthesized bone and the adjacent prosthetic surface which in turn provides a higher degree of mechanical coupling and stability between the prosthesis and the bone.

In a further preferred embodiment, the bone primer composition mixture is provided with a quantity of osteoblasts and/or pluripotent cells prior to application to a patient's bone, i.e. within the medullary canal of a bone which is to receive an endoprosthesis. In this embodiment, osteoblasts and/or pluripotent cells are preferably taken from the patient, for example from bone marrow aspirate or blood plasma as known in the art. These cells can be separated or purified via conventional techniques, and then combined with the bone primer composition mixture to provide an osteoprogenitor cell-enriched bone primer composition mixture. The enriched composition is thus applied, e.g. within the medullary canal, already having a quantity of osteoblasts and or/pluripotent cells interspersed throughout the composition. Once the composition has congealed, osteoblasts can immediately begin synthesizing new bone from bone endogenous material present in the congealed phase.

The invented bone primer can be used to promote bone synthesis and fusion toward (with) any non-cemented endoprosthetic implant, including joint replacement implants and dental posts. The resulting osteogenesis in the intra-medullary gap 18 and bone fusion to the endoprosthetic surface 16 provides an endoprosthesis 30 with a longer useful life. Longer life is due in part to the fact that the prosthesis no longer moves within the medullary canal 18, but rather is stabilized therein shortly following implantation by the compliant barrier layer 10. Further, fusion in-vivo of bone material to the endoprosthetic surface 16 provides lasting stability of the prosthesis within the bone 20.

A further benefit of the invented bone primer composition is that it does not introduce any particulate debris into the medullary canal. Particulate debris, common with conventional bone cements, coated implant surfaces, and structured metallic implant surfaces (e.g. having non-smooth surface topography), has been associated with the onset of osteolysis and subsequent endoprosthetic implant failure.

The invention is not limited to use only for endoprosthetic implantation. The invented bone primer composition can be applied to any bone, anywhere it is desirable to promote bone healing or bone synthesis; e.g. the invented bone primer composition can be applied to fracture fixation (such as fracture healing) in broken bones, or treatment of osteoporotic bone (i.e. to promote osteogenesis and strengthen the bone). The invented bone primer composition is particularly useful to strengthen or repair osteoporotic bone, where there is not a lot of nascent bone material to start with. In this embodiment, the invented bone primer composition promotes accelerated osteogenesis within the osteoporotic bone, thereby strengthening the bone. This can be accomplished with little or no destruction of the osteoporotic bone; e.g. the bone primer composition is simply coated onto the osteoporotic bone, or alternatively, used to fill in defects. In addition, the invented bone primer composition can be used to reconstruct a segmental defect in the case of missing bone, e.g., following tumor resection and/or polytrauma. The invention is particularly useful when applied to or within a spinal cage to enhance spinal fusion via bony ingrowth to the spinal cage.

In general, the invented bone primer composition can be applied anywhere it is desired to promote osteogenesis within or adjacent to bone.

Although the hereinabove described embodiments of the invention constitute the preferred embodiments, it should be understood that modifications can be made thereto without departing from the scope of the invention as set forth in the appended claims. 

1. A composition comprising a bone endogenous material and a degradable polymer material, said degradable polymer material having a half-life for degradation of 1-60 days.
 2. A composition according to claim 1, said bone endogenous material being cross-linked to provide a bone endogenous material scaffold having a first order porosity and a second order porosity.
 3. A composition according to claim 2, said first order porosity having a first order mean Stokes pore diameter of 0.1-300×10⁻¹ meters.
 4. A composition according to claim 2, said second order porosity having mean Stokes pore diameter on the order of 10⁻⁶ meters.
 5. A composition according to claim 2, said second order porosity being provided via degradation of said degradable polymer material, wherein said degradation of said degradable polymer material leaves a tortuous network of tunnels or pores in said composition, said tortuous network of tunnels or pores forming said second order porosity of said bone endogenous material scaffold.
 6. A composition according to claim 1, said bone endogenous material comprising a material selected from the group consisting of fibronectin, collagen, laminin, tenascin, proteoglycans, glycosaminoglycans, fibrinogen, hyaluronic acid, elastin, tricalcium phosphate, hydroxyapatite, other extracellular bone matrix materials, and mixtures thereof.
 7. A composition according to claim 1, said bone endogenous material comprising a material selected from the group consisting of alginates, vitrogens, vitronectins, chitosans, and mixtures thereof.
 8. A composition according to claim 2, further comprising a quantity of growth factors in an effective amount to promote osteoblastic migration through said bone endogenous material scaffold.
 9. A composition according to claim 8, said growth factors comprising factors selected from the group consisting of BMP-7, BMP-4, PDGF-BB, TGF-β1, tetracycline, bFGF, VEGF, PTH, and PTH-rp.
 10. A composition according to claim 8, a portion of said growth factors being in globular protein form.
 11. A composition according to claim 8, a portion of said growth factors being in the form of active peptide fragments.
 12. A composition according to claim 8, said growth factors being covalently linked to polyethylene glycol chains.
 13. A composition according to claim 1, said composition being an aqueous mixture in a flow phase having a viscosity of at least 1 cP at 25° C.
 14. A composition according to claim 1, said composition being in a congealed phase, said composition in said congealed phase having a first order porosity and a second order porosity, said degradable polymer material being degraded, said second order porosity being provided via degradation of said degradable polymer material.
 15. A composition according to claim 14, said degradable polymer material having a half-life for degradation of about 1-7 days.
 16. A composition according to claim 14, said degradable polymer material having a half-life for degradation of less than 1 day.
 17. A composition according to claim 14, said composition having a second order void fraction of 240% based on said second order porosity.
 18. A composition according to claim 1, said degradable polymer material being provided in the form of microspheres or particulates, said composition further comprising growth factors, said growth factors being loaded into said microspheres or particulates of said degradable polymer material.
 19. A composition according to claim 1, said degradable polymer being formulated to include chemical species that are found naturally within osteoclastic resorption lacunae.
 20. A composition according to claim 19, said chemical species comprising tartrate resistant acid phosphatase.
 21. A composition according to claim 1, further comprising a medicament.
 22. A composition according to claim 1, further comprising an osteogenic and/or angiogenic nutrient.
 23. A composition according to claim 1, further comprising a quantity of osteoblasts and/or pluripotent cells.
 24. A method of promoting osteogenesis comprising the steps of: a) providing a composition comprising a bone endogenous material in a flow phase; b) applying said composition to a site within a patient where it is desired to synthesize new bone; c) said composition undergoing a phase transformation from said flow phase to a congealed phase; and d) providing a dual mode porosity system in said composition in said congealed phase, said congealed phase of said composition having a first order porosity and a second order porosity.
 25. A method according to claim 24, said phase transformation being performed by cross-linking said bone endogenous material to provide a bone endogenous material scaffold.
 26. A method according to claim 25, said first order porosity being provided as a characteristic material porosity of said cross-linked bone endogenous material, said first order porosity being determined in part via selection of a cross-linking agent and the degree of cross-linking of said bone endogenous material.
 27. A method according to claim 26, said cross-linking agent comprising an agent selected from the group consisting of thrombin, NDGA, DOPA, lysyl oxidase, genipin, microwaves, ultraviolet light, prolyl hydroxylase, horseradish peroxidase, and mixtures thereof.
 28. A method according to claim 24, said composition further comprising a degradable polymer material, said degradable polymer material degrading to leave a tortuous network of tunnels or pores in said composition in said congealed phase, said tortuous network of tunnels or pores, resulting from said degradation of said degradable polymer material, forming said second order porosity.
 29. A method according to claim 28, said degradable polymer material being provided in an amount sufficient to result in a second order void fraction of 2-40% based on said second order porosity.
 30. A method according to claim 28, said degradable polymer material being provided in the form of microspheres or particulates, said microspheres or particulates having a particle size selected to correspond to a desired pore-size diameter for said second order porosity.
 31. A method according to claim 28, said degradable polymer material comprising a material selected from the group consisting of polylactic acid, polyglycolic acid, polyanhydrides, polyvinyl alcohol, poly [L-lactic acid], poly [D,L-lactic acid], and poly (lactide-co-glycolide) copolymer.
 32. A method according to claim 28, said degradable polymer material comprising a material selected from the group consisting of chitosan, agarose and alginate.
 33. A method according to claim 28, said degradable polymer being formulated to include a chemical species that is found naturally within osteoclastic resorption lacunae, wherein upon said degradation of said degradable polymer, said chemical species is left behind within said second order porosity.
 34. A method according to claim 33, said chemical species comprising tartrate resistant acid phosphatase.
 35. A method according to claim 24, said first order porosity having a mean Stokes pore diameter of 0.1-300×10⁻¹⁰ meters, said second order porosity having a mean Stokes pore diameter on the order of 10⁻⁶ meters.
 36. A method according to claim 24, said first order porosity being effective to accommodate molecular diffusion of nutrient species required by osteoblasts for osteogenesis, and to promote bulk fluid flow or fluid imbibement through said composition in said congealed phase, said second order porosity providing a migratory network for osteoblasts through said composition in said congealed phase without the requirement of prior osteoclastic resorption.
 37. A method according to claim 36, said second order porosity further providing a pathway for angiogenic species and for the synthesis of blood flow pathways to osteoblastic bone synthesis sites.
 38. A method according to claim 24, said second order porosity being provided via a leaching technique, wherein a leachable species is provided to said composition, and is leached out of said composition in said congealed phase leaving behind said second order porosity.
 39. A method according to claim 24, said composition further comprising a quantity of osteoblasts, said osteoblasts, after said composition has undergone said phase transformation and is in said congealed phase, synthesizing new bone from said bone endogenous material present in said congealed phase.
 40. A method according to claim 24, further comprising resecting an end of a bone of said patient, said bone having a medullary canal therein, applying a quantity of said composition, in said flow phase, within the medullary canal to substantially fill said canal with said composition, inserting an endoprosthesis in said medullary canal having said composition therein, and extruding an excess of said composition from said canal to accommodate the volume of said endoprosthesis in the medullary canal.
 41. A method according to claim 40, further comprising reaming said medullary canal prior to applying said composition therein.
 42. A method according to claim 40, said composition undergoing said phase transformation to said congealed phase after insertion of said endoprosthesis in said medullary canal, said congealed composition forming a barrier layer between a surface of said endoprosthesis and a wall of said medullary canal in said bone.
 43. A method according to claim 42, said barrier layer being a compliant barrier layer.
 44. A method according to claim 42, said first order porosity having a radial porosity gradient in said barrier layer, said first order porosity increasing in a radially inward direction from the medullary canal wall to the endoprosthetic surface, and having a first order mean Stokes pore diameter of about 0.1-20×10⁻¹⁰ meters adjacent the medullary canal wall, and a first order mean Stokes pore diameter of about 50-300×10⁻¹⁰ meters adjacent the endoprosthetic surface.
 45. A method according to claim 44, further comprising providing a temperature gradient in said composition between said endoprosthetic surface and said canal wall to induce a magnitude and direction of said radial porosity gradient.
 46. A method according to claim 45, said temperature gradient being provided by heating or cooling said endoprosthesis prior to insertion in said medullary canal.
 47. A method according to claim 44, further comprising coating said canal wall or said endoprosthetic surface with a cross-linking agent to promote increased cross-linking of said bone endogenous material in said composition adjacent said canal wall or said endoprosthetic surface respectively to thereby induce said radial porosity gradient.
 48. A method according to claim 42, said first order porosity providing a pathway for molecular diffusion of nutrient species required by osteoblasts for osteogenesis, and for bulk fluid flow or fluid imbibement through said barrier layer, said second order porosity providing a migratory network for osteoblasts through said barrier layer without the requirement of prior osteoclastic resorption.
 49. A method according to claim 42, further comprising mobilization of osteoblasts from the medullary canal wall through the barrier layer toward the endoprosthetic surface via said second order porosity.
 50. A method according to claim 49, osteoclastic resorption being substantially eliminated.
 51. A method according to claim 48, further comprising cyclically mechanically loading said bone to enhance molecular transport of nutrient species and growth factors via convection through said first order porosity into said barrier layer, said osteoblasts using said nutrient species and said growth factors to synthesize new bone using said bone endogenous material of said barrier layer as raw material for new bone synthesis.
 52. A method according to claim 51, further comprising osteoconverting at least a portion of said bone endogenous material of said barrier layer into new bone via osteoblastic bone synthesis.
 53. A method according to claim 52, further comprising substantially completely converting said barrier layer into new bone.
 54. A method according to claim 51, said cyclic mechanical loading of said bone stimulating bone cells at the medullary canal wall, and inducing bulk fluid flow through said barrier layer via said second order porosity, thereby stimulating recruitment and activity of osteoblasts in said barrier layer.
 55. A method according to claim 51, said cyclic mechanical loading of said bone facilitating diffusion of high-molecular weight factors through said barrier layer, said high-molecular weight factors having a molecular weight greater than 40,000 Da.
 56. A method according to claim 24, said first order porosity providing a pathway for molecular diffusion of nutrient species required by osteoblasts for osteogenesis, and for bulk fluid flow or fluid imbibement through said composition in said congealed phase, said second order porosity providing a migratory network for osteoblasts through said composition in said congealed phase.
 57. A method according to claim 56, further comprising mobilization of osteoblasts through said composition in said congealed phase via said second order porosity.
 58. A method according to claim 57, further comprising osteoconverting at least a portion of said bone endogenous material in said composition in said congealed phase into new bone via osteoblastic bone synthesis.
 59. A method according to claim 58, further comprising substantially completely converting said bone endogenous material in said congealed composition into new bone.
 60. A method according to claim 24, said composition further comprising a medicament.
 61. A method according to claim 24, said composition further comprising a quantity of growth factors in an effective amount to promote osteoblastic migration through said bone endogenous material scaffold.
 62. A method according to claim 61, said growth factors comprising factors selected from the group consisting of BMP-7, BMP-4, PDGF-BB, TGF-b1, tetracycline, bFGF, VEGF, PTH, and PTH-rp.
 63. A method according to claim 61, further comprising covalently linking said growth factors to polyethylene glycol chains, and incorporating said growth factor-linked polyethylene glycol species into said composition in said flow phase, wherein, after said phase transformation of said composition into said congealed phase, the polyethylene glycol chains are covalently bonded to pore surfaces within said first order porosity of said composition in said congealed phase, said growth factors being thereby fixed in place in a substantially uniform distribution throughout said congealed composition.
 64. A method according to claim 61, further comprising a) providing a degradable polymer material, in the form of microspheres or particulates, in said composition, said microspheres or particulates having a particle size selected to correspond to a desired pore-size diameter for said second order porosity; b) loading said growth factors into said microspheres or particulates of said degradable polymer material; c) degrading said degradable polymer material, following said phase transformation of said composition into said congealed phase, to leave a tortuous network of tunnels or pores in said composition in said congealed phase, said tortuous network of tunnels or pores, resulting from said degradation of said degradable polymer material, forming said second order porosity; d) releasing said growth factors as said degradable polymer material degrades, thereby initially concentrating said growth factors within said second order porosity of said composition in said congealed phase, said growth factors being available to osteoblasts migrating through said second order porosity to be used in osteogenesis.
 65. A method according to claim 24, said composition being applied to enhance fracture healing of a broken bone.
 66. A method according to claim 24, said composition being applied to reconstruct a segmental defect to replace missing bone.
 67. A method according to claim 24, further comprising the steps of implanting a spinal cage into said patient's spine, and providing said composition in said spinal cage to enhance spinal fusion.
 68. A compliant barrier layer in an intra-medullary gap between a medullary canal wall of a bone and an endoprosthesis implanted within said medullary canal, said compliant barrier layer comprising a bone endogenous material and having a dual mode porosity system with a first order porosity and a second order porosity, said second order porosity having a larger mean Stokes diameter than said first order porosity.
 69. A compliant barrier layer according to claim 68, said bone endogenous material being cross-linked to provide a bone endogenous material scaffold having said first order porosity and said second order porosity.
 70. A compliant barrier layer according to claim 68, said first order porosity having a radial porosity gradient in said barrier layer, said first order porosity increasing in a radially inward direction from said medullary canal wall to said endoprosthesis, said first order porosity having a first order mean Stokes pore diameter of about 0.1-20×10⁻¹⁰ meters adjacent said medullary canal wall, and a first order mean Stokes pore diameter of about 50-300×10⁻¹⁰ meters adjacent said endoprosthesis.
 71. A compliant barrier layer according to claim 68, said second order porosity having mean Stokes pore diameter on the order of 10⁻⁶ meters.
 72. A compliant barrier layer according to claim 68, said second order porosity being provided via degradation of a degradable polymer material, wherein said degradation of said degradable polymer material leaves a tortuous network of tunnels or pores in said compliant barrier layer, said tortuous network of tunnels or pores forming said second order porosity therein.
 73. A compliant barrier layer according to claim 68, said bone endogenous material comprising a material selected from the group consisting of fibronectin, collagen, laminin, tenascin, proteoglycans, glycosaminoglyeans, fibrinogen, hyaluronic acid, elastin, tricalcium phosphate, hydroxyapatite, other extracellular bone matrix materials, and mixtures thereof.
 74. A compliant barrier layer according to claim 68, said bone endogenous material comprising a material selected from the group consisting of alginates, vitrogens, vitronectins, chitosans, and mixtures thereof.
 75. A compliant barrier layer according to claim 68, further comprising a quantity of growth factors.
 76. A compliant barrier layer according to claim 75, said growth factors being selected from the group consisting of BMP-7, BMP-4, PDGF-BB, TGF-b1, tetracycline, bFGF, VEGF, PTH, and PTH-rp.
 77. A compliant barrier layer according to claim 75, said growth factors being covalently linked to polyethylene glycol chains, said growth factor-linked polyethylene glycol species being covalently bonded to pore surfaces within said first order porosity of said compliant barrier layer, said growth factors being thereby fixed in place in a substantially uniform distribution throughout said compliant barrier layer.
 78. A compliant barrier layer according to claim 75, said growth factors being initially concentrated within said second order porosity of said compliant barrier layer, said growth factors being available to osteoblasts migrating through said second order porosity to be used in osteogenesis.
 79. A compliant barrier layer according to claim 68, exhibiting a strain of 0.01-2.0% during normal physiologic loading of said bone.
 80. A compliant barrier layer according to claim 68, said bone endogenous material being initially present in said compliant barrier layer in an amount of at least 50 weight percent on a dry basis. 